APPLICATIONS |
| |
| INDUSTRIAL: |
THERMAL INSULATION OF PIPE LINE, EQUIPMENTS, HORTON SPHERES, VESSEL, ETC. |
| |
| BUILDINGS |
ROOF INSULATION. WALL INSULATION,
PRE FABRICATED INSULATED PANELS ETC, AND MOST SUITABLE FOR REFRIGERATED VANS/TRUCKS ETC.
|
| |
| Advantages: |
- Lower thickness of insulationis enough,compared to other materials.
- Lower thermal diffusivity ofsunfoam will resultin lower rise in conditioned temerature in covered area.
- Sunfoam be used for dual temperature systems applications.
- Sunfoam could be made to custom built against specific order suit any contour,even with overlapping joints.
- Sunfoam moulded products come with water resistant skin, thus need no extra facing.
- Sunfoam is conversant & adaptable to all conditions and applications.
|
| |
| MANUFACTURED BY |
|
| New no 113, old no 204, |
| SIDCO INDUSTRIAL ESTATE |
| AMBATTUR, CHENNAI 600 098 |
| Phone No: 044 26258802/26154752 |
| Fax: 044 26258802 |
| Mobile: No: 98410 70349 |
| Email:sunpreeth2000@yahoo.com |
| |
|
| PRODUCT |
Sunfoamis a rigid polyurethane foam material, available in the form ofSLABS, PIPE SECTIONS. PIPE SUPPORTS AND INSITU FOAMING
for thermal insulation |
| |
| STANDARDS |
SUNFOAM CONFIRMS TO I S 12436. |
| |
| SLABS: |
| STANDARD SIZE |
1000 MM X 500 MM X VARIOUS THICKNESS |
| |
| SPECIAL SIZE |
2000MM X 100 MM X VARIOUS THICKNESS
RANGING FROM 20 MM TO 200 MM AND DENSITY RANGING FROM
34 Kg+ or – 2 Kg/ Cu.M TO 60 Kg + or – 2 Kg/Cu.M
|
| PIPE SECTIONS: |
TO SUIT 12 MM NB TO 750 MM NB |
WALL THICKNESS RANGING FROM 25 MM TO 150 MM |
STD. LENGTH : 1000 MM |
SPECIFIC DIMENSIONS CAN BE MADE TO ORDER, PIPE SECTION CAN BE SUPPLIED IN 2 & 3 LAYERS FOR THICKNESS ABOVE 75 MM |
- Density : 38 +or- 2 kg/ Cu. M.
- Compressive Strength : 280 (KPa)
- Tensile Strength : > 1.8 kg/Cm2 (ASTM 1621 – 64).
- Close cell content : > 90%
- Thermal Conductivity(K) : 0. 018 W / m deg k .
- Ignitability (ASTM D 1699 : Fire retardant, not easily ignitable.
(Class P)
|
| |
| PIPE SUPPORTS: |
MANUFACTURED TO SUIT 12 MM NB PIPE TO 750 MM NB PIPES SLIDE TYPE, ANCHOR TYPE & GUIDE TYPE SUPPORTSDENSITY RANGING FROM 60 Kg/Cu.m TO 300 Kg/Cu.M. |
| |
| Marketed By |
Sonjay Engineering Services |
11/10, 1 st Main road, Jai Nagar, |
ARUMBAKKAM, Chennai 600 106. |
Phone 26258802 |
Mobile: 9841070349 / 9841272265/9841272258 |
| |
 |
Pipe supports are made from specially formulated Chemical system that results in the most adaptable Material with several advantages |
| |
| Wide density range |
Higher densities enable higher loads with out increase in surface area Lower densities can be used for lighter loads resulting in significant cost saving. |
| |
| Pre engineered at factory |
supports precisely match the Pipe’s OD, No sawing or Shaping at site
|
| ‘K’ Value ( Excellent) |
Superior insulation as compared to wood and other insulation materials No condensation at support points. So no drips, puddles, save energy |
| |
| Close cell structure |
Does not permit water penetration, so no wet rotting or dry rotting |
| |
| Good fire resistance |
They are fire retardant, improves safety and durability at site.
|
| Dimensional & non standard Shapes and sizes |
Supports are so adaptable in nature while manufacturing that it can
made in any shape desired or size with different densities, resulting
In precisely matched supports with neat finish at the support location |
| |
PHYSICAL PROPERTIES FOR DIFFERENT DENSITIES
|
DENSITY
(Kg/m3) |
CLOSED CELL % |
WATER VAPOUR
TRANSMISSION
(gms/m2/24hrs) |
COMPRESSION
STRENGTH(kPa) |
TENSILE
STRENGTH(Kpa) |
80 |
93 |
50 |
900 |
1200 |
120 |
94 |
45 |
1500 |
1600 |
180 |
94 |
30 |
2900 |
2500 |
250 |
96 |
25 |
4900 |
3100 |
320 |
96 |
15 |
8200 |
5000 |
|
| |
COMPARISON
WITH WOOD
|
| WOOD |
DENSITY
(Kg/m3) |
'K' VALUE AT
10oC |
MAX TEMP
oC |
MIN TEMP
oC |
FIRE
RATING |
OAK |
740 |
0.159 |
65 |
>0 |
POOR |
MAHAGONY |
560 |
0.144 |
65 |
0 |
POOR |
|
SUN FOAM
|
80 |
0.023 |
110 |
-185 |
Class P BS:476/5 |
| supports |
120 |
0.033 |
110 |
-185 |
-do- |
| |
180 |
0.033 |
110 |
-185 |
-do- |
| |
250 |
0.035 |
110 |
-185 |
-do- |
|
| |
| |